低TiO2 、低SiO2、低F
在特殊鋼精煉過程中應(yīng)用效果顯著
您的位置：首頁 > 產(chǎn)品展示 > 合成鈣鋁渣
低TiO2 、低SiO2、低F
在特殊鋼精煉過程中應(yīng)用效果顯著
| 型號(hào)成分(%) | 特鋼09 | 特鋼08 | GL-50 | GL-80 | 燒結(jié)GL |
| CaO | 41-49 | 43-47 | 45-49 | 45-55 | 45-55 |
| Al2O3 | 36-44 | 36-44 | 32-38 | 38-48 | 38-45 |
| TiO2 | ≤0.09 | ≤0.08 | ≤1.5 | ≤1.8 | ≤1.0 |
| SiO2 | ≤3.0 | ≤3.0 | ≤5.0 | ≤8.0 | ≤5.0 |
| Fe2O3 | ≤1.0 | ≤1.0 | ≤1.5 | ≤1.5 | ≤1.5 |
| MgO | ≤3.0 | 10-15 | ≤4.0 | ≤5.0 | ≤4.0 |
| F | ≤0.01 | ≤0.05 | ≤1.0 | ≤1.0 | ≤1.0 |
| 型號(hào)成分 |
特鋼09 |
特鋼08 |
GL-50 | GL-80 |
燒結(jié)GL |
|
水分(%) |
≤0.5 | ≤0.5 | ≤0.5 | ≤0.5 | ≤0.5 |
|
粒度(%) |
3-30mm ≥90 |
3-30mm ≥90 |
3-50mm ≥90 |
3-50mm ≥90 |
3-40mm ≥90 |
低熔點(diǎn)
高堿度
高硫容量
低氧化性
| 型號(hào)成分(%) | LL-TiO2 03 | L-TiO2 09 | H-AI2O3 | H-CaO |
| CaO | 40-55 | 42-52 | 30-42 | 50-58 |
| Al2O3 | 30-55 | 34-44 | 50-60 | 32-42 |
| TiO2 | ≤0.04 | ≤0.09 | ≤2.0 | ≤2.0 |
| SiO2 | ≤3.0 | ≤3.0 | ≤5.0 | ≤5.0 |
| Fe2O3 | ≤1.0 | ≤1.0 | ≤2.5 | ≤2.5 |
| MgO | ≤3.0 | ≤4.0 | ≤4.0 | |
| F | ≤0.1 | ≤0.1 |
| 型號(hào)成分 | LL -TiO2 03 | L-TiO2 09 | H-AI2O3 | H-CaO |
|
水分(%) |
≤0.5 | ≤0.8 | ≤0.5 | ≤0.5 |
|
粒度(%) |
3-40mm ≥90 |
3-40mm ≥85 |
3-50mm ≥90 |
3-50mm ≥90 |
| 型號(hào) 成分(%) | YH-A | YH-B |
| M-AI | 30-40 | 25-30 |
| CaO | 20-30 | 20-30 |
| SiO2 | ≤10 | ≤10 |
| Al2O3 | ≤5 | ≤10 |
| Fe2O3 | ≤2.0 | ≤2.0 |
| 型號(hào) 成分 | YH-A | YH-B |
|
水分(%) |
≤1.5 | ≤1.5 |
|
粒度 |
扁球狀 6-40mm |
扁球狀 6-40mm |
| 型號(hào)成分(%) | HDG-30 | HDG-10 | HJL-15 |
| Al | 28-32 | 8-12 | 10-15 |
| CaO | 20-35 | 25-40 | ≥50 |
| Al2O3 | 15-25 | 20-30 | ≥5.0 |
| SiO2 | ≤6.0 | ≤6.0 | ≤8.0 |
| CaF2 | 2-6 | 5-9 | |
| MgO | 5-10 | 5-10 |
| 型號(hào)成分 | HDG-30 | HDG-10 | HJL-15 |
|
粒度 |
5-40mm | 5-40mm |
3-30mm ≥90% |